Blowing agents of the tetrazoles and their derivatives

ABSTRACT

Blowing agents of tetrazoles and their derivatives which have a melting point over 200° C. and are used to manufacture the high quality foaming thermoplastic synthetic resin moldings, especially engineering or superengineering plastic moldings and said blowing agents generate no harmful gases and do not cause the deterioration of the thermoplastic synthetic resin moldings.

This is a divisional of Ser. No. 07/941,836, filed Sep. 8, 1992 which is a pending continuation-in-part of Ser. No. 07/798,561 filed Nov. 26, 1991.

BACKGROUND OF THE INVENTION

(1) Field of the Invention

The present invention relates to tetrazole blowing agents and their derivatives which are used to manufacture foamed thermoplastic resin moldings (hereinafter referred to as the cell structured artificial plastics) which have a high melting point and high softening point, i.e. the tetrazoles and their derivatives are the blowing agents to be used for the cell structured artificial plastics which have high quality and have no shrink and no warp and accordingly have various uses.

(2) Description of the Prior Art

Formerly, as the blowing agents for the manufacture of foamed thermoplastic synthetic resins, liquid hydrocarbons or volatile hydrocarbons such as propane, butane, pentane and heptane or the blowing agents which are decomposed at low temperature such as diazo type blowing agents were used in the fixed molding process.

SUMMARY OF THE INVENTION

Formerly, blowing agents which were used for the ordinary foamed synthetic resin plastic moldings are low in vaporization temperature and thermal decomposition temperature and so the synthetic resins in which are used said blowing agents are limited to the ordinary synthetic resins which have low melting points, but recently thermoplastic engineering plastic moldings have been in increased demand, and moreover due to the development of thermoplastic superengineering plastic moldings containing liquid crystals, the demand for the high quality cell structured artificial plastics is increasing. However, generally, ordinary blowing agents are not used for engineering plastic moldings or superengineering plastic moldings which have high melting points or high softening points compared with ordinary thermoplastic moldings and so, the above described high quality foamed resins are not manufactured by using the said ordinary blowing agents.

The object of the present invention is to provide blowing agents which have the following properties (a)-(c) such that they may be used in the manufacture of high quality thermoplastic synthetic resin moldings:

(a) The thermal decomposition temperatures are at least over 200° C.

(b) A large quantity decomposition gases (non-toxics) are generated, accompanied by the decomposition of the blowing agents.

(c) The decomposition gases do not include gases which cause the deterioration or degradation of the thermoplastic synthetic resins to occur, such as ammonia or alcohol.

DETAILED DESCRIPTION OF THE INVENTION

To attain the above described object, the present inventors confirmed that the below described tetrazoles and their derivatives satisfy the above properties (a)-(c). As the result of their investigation, the present inventors have discovered that by using these tetrazoles and their derivatives as blowing agents, the manufactured cell structured artificialplastics have no shrink and warp and the manufactured products are excellent, and so the inventors of the present invention completed the present invention. Namely the present invention relates to single or plural tetrazoles and their derivatives which have the following structural formulas used for the manufacture of the foamed thermoplastic synthetic resins. ##STR1##where R and R₁ are the same or different and are selected from the group consisting of H, C₁ to C₆ alkyl, C₃ to C₆ cycloalkyl, C₂ to C₆ alkenyl radicals optionally substituted by one or more C₁ to C₆ alkyl, --OH, --COOH, SO₃ H, NO₂, halogen and --NR₄ R₅, wherein R₄ and R₅ may each be H or C₁ -C₄ alkyl or R and R₁ can be phenyl, benzyl or phenethyl radicals optionally substituted by 1 to 3 halogens, --OH, NO₂, --CN, --COOH and NR₄ R₅ wherein R₄ and R₅ are as defined above;

R₂ is selected from H, --OH, --COOH, --SO₃ H, --NO₂, halogenor --NH₄ R₅ wherein R₄ and R₅ are as defined above, C₁ to C₆ alkyl, C₃ to C₆ cycloalkyl or C₂ to C₆ alkenyl, optionally substituted by C₁ to C₆ alkyl, --OH, --COOH, --SO₃ H, --NO₂, halogen, --NR₄ R₅ wherein R₄ and R₅ are as defined above or R₂ can be phenyl, benzyl or phenethyl radicals optionally substituted by 1 to 3 halogens, --OH, NO₂, --NR₄ R5, wherein R₄ and R₅ are as described above, C₁ to C₄ alkyl and esters or amides of lower carboxylic acids;

R₃ is selected from the group consisting of C₅ to C₆ alkylene, cycloalkylene, or alkenylene, optionally substituted by C₁ to C₆ alkyl, --OH, --COOH, SO₃ H, --NO₂, halogen or NR₄ R₅, wherein R₄ and R₅ are as defined above, the alkylene, cycloalkylene or alkenylene radicals optionally containing --O--, --S--, --SO₂, --CO--, phenylene and bisphenylene being optionally substituted by 1 to 8 halogens, --OH, --NO₂, esters or amides, lower carboxylic acids, --NR₄ R₅ wherein R₄ and R₅ are as defined above, C₁ to C₄ alkyl;

M is a divalent metal selected from Ca, Cu, Zn, Mn, Fe, Co, Ni and Ba, and Z is a univalent inorganic or organic radical which may bind to or form a salt with M, such as SO₄, NH₄, --HCO₃, --HPO₄, --NO₃, --ONH₄, --CH₃, --C₂ H₅, --CHO, NH₂ orSO₃ H.

One or more of the above compounds may be employed and the compounds employed have higher melting points or the softening points than the thermoplastic synthetic resins used, and the amount of the above tetrazolederivatives employed is 0.01-15 weight % per 100 weight % of the thermoplastic synthetic resins.

In the case where the amount of blowing agents used is under 0.01 weight %,the foaming degree of the thermoplastic synthetic resins is inferior, and in the case when the amount of the blowing agents used is over 15%, such amount of blowing agents is excessive and thus the foamed synthetic resin molding properties and the resultant foamed molding products are inferior,and thus, both cases can not be used in the present invention.

As described above, the blowing agents of the present invention have the higher thermal decomposition temperature than the melting points or the softening points of the thermoplastic synthetic resins used, and furthermore the thermal decomposition points of the blowing agents are very sensitive to the thermal decomposition at a higher molding temperature than the temperature of melting points or softening points of the thermoplastic synthetic resins.

A fixed quantity of the blowing agents is added to the master batch (polymer premixed with concentrated blowing agents) of the thermoplastic resins treated previously to make a chip or pellet which has mutual solubility with the thermoplastic synthetic resins and the thus treated thermoplastic synthetic resins are used for molding.

The thermoplastic synthetic resins to be used for the present invention arenot especially limited, but the thermoplastic resins which can be used for the present invention are selected from the below described group, i.e. polyolefins, fluoropolymers, acrylonitrile-butadiene-styrene resins, polystyrene, polyvinyl chloride (PVC) polyacrylates, polyamide, polycarbonate (PC), polyphenylene oxides (PPC), polyethylene terephthalates (PEC), polybutylene terephthalates (PET), polyphenylene sulphides (PPS), polyether sulfones (PES), polyimide amides (PAI), polyether imides (PEI), polyether ether ketones (PEEK), polysulfonates (PSF), liquid crystal polymers (LCP), polytetrafluoroethylene (PTFE) or their copolymers or polymers.

And the antioxidant, ultraviolet light absorption reagents, dyes, pigments,fillers or the reinforcing fibers, etc., can be blended with the thermoplastic resins.

In order to manufacture the thermoplastic synthetic resin moldings of the present invention, injection molding, extrusion molding, blowing molding, press molding or any other molding can be used.

For instance, in injection molding, the amount of additional tetrazole blowing agents used in the molding machine is selected according to the purpose of the molding product and these blowing agents are mixed with thethermoplastic synthetic resins and the mixed products are injection molded by the ordinary method or by the extrusion molding method by using a 2 axis extrusion molding machine.

The desired thermoplastic synthetic resins and tetrazole blowing agents which are mixed with the thermoplastic synthetic resins are separately introduced into the hopper and firstly the desired thermoplastic syntheticresins are separately introduced into the hopper and then the fixed amount of desired thermoplastic synthetic resins is extruded, and thermoplastic resins mixed with the tetrazole blowing agents are extruded according to the ordinary molding method. In this case, in order to prevent shrink and warp, the full shot method or slightly shot method of molding are preferable, and also it is preferable that the metal mold is kept under slightly reduced pressure or slightly short shot to obtain a comparativelyhigher foaming rate. And moreover, in the case of the injection molding method, by using the coinjection molding, from the same or different thermoplastic synthetic resins mixed with the blowing agents of the present invention, different kinds of thermoplastic synthetic resins can be manufactured where the non-foamed thermoplastic synthetic resins exist at the surface layer and the thermoplastic synthetic resins having the foams with high ratio exist in the interior of the product, and injection moldings which shrink and warp are improved so that they may be used in applications which require surface smoothness and dimensional accuracy.

And moreover, by using an extruder, various types of extrusion moldings canbe manufactured by the conventional method e.g. fibers or films or sheets or other various types of extrusion foamed moldings using the thermoplastic synthetic resins including the blowing agents of the presentinvention.

And, by using the blowing agents of the present invention, from the foamed thermoplastic synthetic resin portions together with the non-foamed thermoplastic synthetic resin portions, the conjugate fibers or coextrudedfibers or sheets, extruded laminate fibers or sheets can be manufactured.

And also, instead of the manufactured thermoplastic synthetic resin portion, paper, metals, ceramics or other materials can be used. These foamed moldings have the characteristics of light weight, adiabatic property, good cushioning property, beautiful appearance and shielding of light and have various available uses.

EXAMPLE Example 1

(1H)-tetrazole (decomposition temperature 241° C.) is added to the copolymerized nylon based on 12-Nylon [--NH(CH₂)₈ CO-]poly(9-amino nonanoic acid) 5 weight % and melted and the chips are made from them, and these chips are mixed with the 6-Nylon [NH(CH₂)₃ CO]poly (melting point 215° C.) 6.25, 8.0, 4.0 weight % each and then these are injection molded using test metal mold (length 60 mm, breadth 40 mm and thickness 5 mm) according to the conditions of Table 1 and the results are summarized in Table 1.

                  TABLE 1                                                          ______________________________________                                         Addition                                                                              Injection                   Foaming                                     Quantity                                                                              Tempera- Molding   Condi-                                                                               Specific                                                                              Rate                                    (%)    ture (°C.)                                                                       Tem. (°C.)                                                                        tion  Gravity                                                                               (Multiple)                              ______________________________________                                          0.125 250      70        No. 1 1.13   1.002                                                             2     1.10   1.025                                                             3     1.06   1.050                                                             4     1.05   1.075                                                             5     0.99   1.125                                   0.25                      No. 1 1.12   1.005                                                             2     1.07   1.050                                                             3     1.05   1.075                                                             4     0.95   1.125                                                             5     0.94   1.175                                   0.50                      No. 1 1.10   1.025                                                             2     1.05   1.060                                                             3     1.02   1.100                                                             4     0.95   1.175                                                             5     0.90   1.250                                   ______________________________________                                         Wherein: Injection conditions are as follows:                                  No. 1 full shot                                                                No. 2 3.7% short shot                                                          No. 3 7.4% short shot                                                          No. 4 11.1% short shot                                                         No. 5 14.5% short shot                                                    

Example 2

Molding results by the full shot injection condition are summarized in Table 2.

                                      TABLE 2                                      __________________________________________________________________________             Decom-               Property of                                          Blowing                                                                             posi-                                                                               Kind of         Molding foam-                                        Agent                                                                               tion thermo-                                                                             Molding                                                                             Foaming                                                                              ing form                                             Addition                                                                            Temp.                                                                               plastic                                                                             Temp.                                                                               Rate  formability                                       NO Quantity                                                                            (°C.)                                                                        resins                                                                              (°C.)                                                                        (Multiple)                                                                           (shrink, warp)                                    __________________________________________________________________________     1  (a)  283  Modified                                                                            290  1.002 Surface,                                             0.125     PPE             beautiful                                                                      no shrink                                                                      no warp                                           2  (b)  285  PC   300  1.004 Surface,                                             0.200                     beautiful                                                                      no shrink,                                                                     slightly                                                                       warp                                              3  (c)  276  PET  285  1.003 Surface,                                             0.125                     beautiful                                                                      no shrink,                                                                     no warp                                           4  (d)  276  PBT  280  1.003 Same as                                              0.200                     above                                             5  (e)  262  66   275  1.002 Same as                                              0.125     Nylon           above                                             __________________________________________________________________________

Wherein: Structural formula of the used tetrazoles in Table 2 (a)-(e) are as follows: ##STR2##Wherein p is the para position and Ph is phenyl.

Example 3

The results of molding of 10% short shot injection molding are summarized in Table 3.

                                      TABLE 3                                      __________________________________________________________________________             Decom-               Property of                                          Blowing                                                                             posi-                                                                               Kind of         Molding foam-                                        Agent                                                                               tion thermo-                                                                             Molding                                                                             Foaming                                                                              ing form                                             Addition                                                                            Temp.                                                                               plastic                                                                             Temp.                                                                               Rate  formability                                       NO Quantity                                                                            (°C.)                                                                        resins                                                                              (°C.)                                                                        (Multiple)                                                                           (shrink, warp)                                    __________________________________________________________________________     1  (a)  282  Modified                                                                            290  1.092                                                   Foaming, fine                                                                     0.125     PPE                                                               surface, good                                                                  no shrink,                                                                                                  no warp                                           2  (b)  285  PC   300  1.104 Same as                                              0.200                     above                                             3  (c)  276  PET  285  1.093 Same as                                              0.125                     above                                             4  (d)  276  PBT  280  1.098 Same as                                              0.200                     above                                             5  (e)  262  66   275  1.089 Same as                                              0.125     Nylon           above                                             __________________________________________________________________________

Wherein: (a)-(e) in Table 3 are same as in Table 2.

Example 4

After mixing 5 weight % powder of the 1-p-nitrophenol-5-ethyl- tetrazole with the copolymerized polyester powder (M.P. 140° C.), this mixture is melt extruded and granulated, and a fixed amount of the granulated particles is mixed with the polyethylene terephthalate resin chips having the limiting viscosity 0.72 (measured in the solution of tetrachloroethane/phenol=2:3 at 30° C.) and these are dried under reduced pressure and after regulating the water content to under 50 ppm, the temperature of the resins is raised to 280° C. and the resultant resin is melted, extruded as a roll, and solidified on cooling and formed into a sheet having a thickness of 5 mm. The properties of the obtained sheets are summarized in Table 4.

Comparative Experiment 1

Polyethylene terephthalate resins which are the same as used in Example 4, are melted and manufactured, the extruded sheets are formed under the sameconditions as Example 4 and the properties of sheet are recorded in Table 4.

                  TABLE 4                                                          ______________________________________                                         Blowing Agent                      Foaming                                     Addition                    Den-   Rate                                        Quantity (5)    Appearance  sity   (multiple)                                  ______________________________________                                         Experi-  0.125      White Opaque                                                                               1.20 1.12                                      ment 4  0.25        Same as above                                                                              1.11 1.21                                              0.50        Same as above                                                                              1.02 1.32                                      Compara-                                                                               --          Semitrans-  1.35 --                                        tive Ex-            parent                                                     periment 1                                                                     ______________________________________                                    

Example 5

Crystalline Cu salt of 5-methyl-1H-tetrazole (a) (decomposition temperature(287° C.) which is finally pulverized with the mortar is added in the amount shown by Table 5 to the PPS (polyphenylene sulphide) M.P. 227°0 C.) and mixed carefully so that (a) adheres uniformly to the chip surface of the PPS and the chips are melted and injection molded under the same conditions shown in Table 5, and the results are summarizedin Table 5.

                  TABLE 5                                                          ______________________________________                                                                             Foaming                                    Addition                                                                              Injection  Die Temp. Injection                                                                              Rate                                       Qty (%)                                                                               Temp. (°C.)                                                                        (°C.)                                                                             Condition                                                                              (multiple)                                 ______________________________________                                          0.125 320        140       No. 1   1.002                                                                  2       1.025                                                                  3       1.05                                                                   4        .075                                                                  5       1.125                                      0.25                        No. 1   1.005                                                                  2       1.50                                                                   3       1.075                                                                  4       1.125                                                                  5       1.175                                      0.50                        No. 1   1.025                                                                  2       1.060                                                                  3       1.100                                                                  4       1.175                                                                  5       1.125                                      ______________________________________                                         Wherein: Injection condition                                                   No. 1: full shot                                                               No. 2: 3.7% short shot                                                         No. 3: 7.4% short shot                                                         No. 4: 11.1% short shot                                                        No. 5: 14.5% short shot                                                   

Example 6

According to Example 3, the foamed plastics are manufactured using various plastics and the results are summarized in Table 6.

                                      TABLE 6                                      __________________________________________________________________________             Decom-               Property of                                          Blowing                                                                             posi-                                                                               Kind of         Molding foam-                                        Agent                                                                               tion thermo-                                                                             Molding                                                                             Foaming                                                                              ing form                                             Addition                                                                            Temp.                                                                               plastic                                                                             Temp.                                                                               Rate  formability                                       NO Quantity                                                                            (°C.)                                                                        resins                                                                              (°C.)                                                                        (Multiple)                                                                           (shrink, warp)                                    __________________________________________________________________________     1  (a)  287  PPS  320  1.002                                                   Surface                                                                           0.125                     beautiful                                         no shrink,                                                                                                  no warp                                           2  (b)  322  PEI  360  1.007 Same as                                              0.150                     above                                             3  (c)  363  PES  370  1.013 Same as                                              0.200                     above                                             4  (d)  376       390  1.003                                                   Surface                                                                           0.125                     beautiful                                         No shrink,                                                                                                  no warp                                           5  (e)  399  PPEK 400  1.506 Same as                                              0.150                     No. 1                                             __________________________________________________________________________

Wherein: The blowing agents used in the Table 6 are as follows: ##STR3##Wherein: Pr is --CH₂ CH₂ CH₃

Example 7

Similar to Examples 3 and 4, blowing agents are added to the thermoplastic synthetic resins described in Table 7 and molded to 10% short shot, and the results are summarized in Table 7.

                                      TABLE 7                                      __________________________________________________________________________             Decom-               Property of                                          Blowing                                                                             posi-                                                                               Kind of         Molding foam-                                        Agent                                                                               tion thermo-                                                                             Molding                                                                             Foaming                                                                              ing form                                             Addition                                                                            Temp.                                                                               plastic                                                                             Temp.                                                                               Rate  formability                                       NO Quantity                                                                            (°C.)                                                                        resins                                                                              (°C.)                                                                        (Multiple)                                                                           (shrink, warp)                                    __________________________________________________________________________     1  (f)  287  PPS  320  1.062                                                   Foaming                                                                           0.125                     fine                                              Surface                                                                                                     beautiful                                         no shrink,                                                                                                  no warp                                           2  (g)  322  PEI  360  1.118 Same as                                              0.1                       above                                             3  (h)  363  PES  370  1.125 Same as                                              0.200                     above                                             4  (i)  376       390  1.073 Same as                                              0.125                     above                                             5  (j)  399  PPEK 400  1.119 Same as                                              0.150                     No. 1                                             __________________________________________________________________________

Wherein: The blowing agents (f)-(j) in Table 7 are as follows: ##STR4##Wherein: Pr is --CH₂ CH₂ CH₃

EFFECTS OF THE INVENTION

The effects of the present invention are summarized as follows:

(1) The invention of the blowing agents for use with high quality thermoplastic synthetic resins which have a high melting point or high softening point are accomplished by the present invention.

(2) Thermal decomposition of the tetrazole derivatives is complete and the main ingredient of the decomposed gases is nitrogen and thus has no harmful effects on the thermoplastic synthetic resin moldings, for instance, deterioration etc. of the moldings.

(3) It is possible by the present invention to give a foamed structure to the thermoplastic engineering and superengineering plastics which were formerly difficult to produce.

(4) The foamed moldings of the present invention may be formed as fibers, films, sheets or 3-dimensional moldings by using the ordinary molding method, e.g. extrusion, injection, blowing or press molding.

(5) In addition to the characteristics of the engineering and superengineering plastic moldings which themselves have high heat resistance and high mechanical properties, the foamed thermoplastic synthetic resin moldings which are manufactured by the present invention have the characteristics of light and beautiful surface appearance and no shrink and warp. 

What we claim is:
 1. In a process for the production of cellular products which comprises incorporating a blowing agent into rubber or a synthetic polymer and then heating to activate the blowing agent, the improvement which comprises using as the blowing agent tetrazole compounds represented by the formulae (II), (III) and (V): ##STR5## wherein R₂ is selected from the group consisting of H, --OH, --COOH, --SO₃ H, --NO₂, halogen and --NH₄ R₅ wherein R₄ and R₅ each are H or C₁ to C₄ alkyl, C₁ to C₆ alkyl, C₃ to C₆ cycloalkyl or C₂ to C₆ alkenyl, optionally substituted by C₁ to C₆ alkyl, --OH, --COOH, --SO₃ H, --NO₂, halogen, --NR₄ R₅ wherein R₄ and R₅ are as defined above or, R₂ can be phenyl, benzyl or phenethyl radicals optionally substituted by 1 to 3 halogen, --OH, NO₂, --NR₄ R₅, wherein R₄ and R₅ are as described above, C₁ to C₄ alkyl and esters or amides of lower carboxylic acids;R₃ is selected from the group consisting of C₅ to C₆ alkylene, cycloalkylene or alkenylene, unsubstituted or substituted by C₁ to C₆ alkyl, --OH, --COOH, SO₃ H, --NO₂, halogen, NR₄ R₅ wherein R₄ and R₅ are as defined above, --O--, --S--, --SO₂, --CO--, --phenylene or bisphenylene, said phenylene or bisphenylene being unsubstituted or substituted by 1 to 8 halogens, --OH, --NO₂, esters or amides of lower carboxylic acids, NR₄ R₅, wherein NR₄ and R₅ are as defined above or C₁ to C₄ alkyl; and M is a divalent metal selected from Ca, Cu, Zn, Mn, Fe, Co, Ni and Ba.
 2. The process of claim 1 which includes heating the polymer containing said tetrazole compounds to a temperature sufficient to decompose the tetrazole compounds.
 3. The process of claim 1 which comprises directly adding the tetrazole compound as blowing agent to a synthetic thermoplastic polymer or its components for the production of cellular products.
 4. The process of claim 1 which includes, after said incorporating and prior to heating, the step of forming the polymer with the tetrazole compound therein at a temperature less than the decomposition temperature of the tetrazole, into formable chips or pellets.
 5. The process of claim 1 in which the blowing agent is employed in an amount of from about 0.01 to about 15 percent by weight of the rubber or synthetic polymer. 